Opis proizvoda

In principle, a prepolymer could be formed by reacting diisocyanates with an excess of polyol to produce a polyol functional prepolymer with urethane functionality at its center, but this is not practiced commercially and the term "prepolymer" is always used to refer to polyols terminated with isocyanate functionality. The excess isocyanate is required to prevent molecular weight growth caused by opportunistic chain extension of unreacted polyol reacting with the isocyanate-terminated prepolymer. In practice, chain extension always occurs but can be limited by increasing the ratio of isocyanate to hydroxyl functionality. A true "prepolymer" in this regard would then distill the excess isocyanate from the product. In the case where the excess isocyanate is left in the product, this is referred to as a "quasi-prepolymer". In practice, quasi-prepolymer refers to systems with relatively high levels of free isocyanate (>12%), dok se predpolimer odnosi na sisteme sa niskim nivoom slobodnih izocijanata (<12%). Overall, over 400 million pounds a year of prepolymer is used commercially for many applications where the advantages of prepolymers can be realized.

Ovaj poliuretanski predpolimer na bazi kvazi-MDI estera sastoji se od tri komponente A/B/C. Komponenta A je kvazi-MDI poliesterski predpolimer koji je završio sa izocinatom, komponenta B je poliester poliol, komponenta C je 1,4BDO.

Njegovi kvazi predpolimerni sistemi mogu pružiti određene prednosti u odnosu na konvencionalnije potpune predpolimere nudeći predpolimere i sredstva nižeg viskoziteta, nižu temperaturu materijala za obradu, elastomere više tvrdoće sa istim sistemom, kao i bolju zaštitu životne sredine i zdravlja.

Glavna prednost leži u kratkom vremenu vađenja iz kalupa, što omogućava povećanu produktivnost.

Prednost

• Odlična mehanička svojstva
• Podesiva reaktivnost, odnosno izbor odnosa katalizatora i smeše
• Pogodno za livenje veoma velikih delova
• Održive alternative sistemima koji se mogu suočiti sa regulatornim ograničenjima
• Smanjena potrošnja energije za veću održivost

Sistemi na bazi kvazi-MDI estera nude vrhunsku otpornost na habanje i kidanje uz odličnu otpornost na hemikalije kao što su ugljovodonici, ulja i rastvarači. Ovi sistemi su idealan izbor za aplikacije kao što su sita, strugači, PIG, betonske oštrice, listovi i vibracione posude.

Tipični indikatori:

Stavka	BQ{0}}B			BQ{0}}A			BQ{0}}C
Dočasnički sadržaj/%	16.5±0.2			-			-
Radna temperatura/stepen	45			70			45
Viskoznost MPa-s	700			730			30
Pre-polimer	BQ{0}}B
Produživač lanca	BQ3516-A+BQ3516-C
Tvrdoća/Shore A	55	60	65	70	75	80	85	90
BQ3516-B (omjer, po težini)	100	100	100	100	100	100	100	100
BQ3516-A (omjer, po težini)	380	180	160	130	110	100	80	60
BQ3516-C (omjer, po težini)	0	9.1	10	11.4	12.3	12.7	13.6	14.5
Katalizator/ukupna težina/(A+B+C)(%)	0.4	0.4	0.4	0.4	0.3	0.3	0.3	0.3
Temperatura kalupa/stepen	100
Vrijeme geliranja/min	5	5	5	5	5	4	4	4
Vrijeme skidanja/min	50	35	35	30	30	30	30	30
Vreme posle sušenja (100 stepeni)/h	16

Fizička svojstva

Tvrdoća/Shore A	55	60	65	70	75	80	85	90
Vlačna čvrstoća/MPa	16	36	43	46	48	49	50	50
Izduženje pri prekidu/%	950	600	550	550	550	550	500	500
100% modul/MPa	1.4	2.2	2.4	3.7	4.6	5.2	6.6	9.6
300% modula/MPa	1.5	4.2	5.2	7.2	11.4	11.1	14.6	19.2
Čvrstoća na kidanje (bez Nicka) /(KN/m)	23	55	66	78	88	98	106	125
Snaga kidanja (sa Nickom) /(KN/m)	11	21	29	34	38	44	56	63
Odskok (23 stepena)/ %	56	50	50	48	47	47	46	44
Gubitak abrazije/mm³/(DIN)	11	12	14	15	15	17	19	22
Set kompresije/% (22 sata/70 stepeni)	15	17	19	21	24	26	29	32
Specifična težina (25 stepeni) (g/cm³)	1.17	1.18	1.19	1.19	1.2	1.21	1.22	1.22